Carbon fabric 160 g/m² (twill weave), width 125 cm/100cm
Carbon fabric 160 g/m² (twill weave), width 125 cm
In stock
Glass fabric tape 49 g/m² (Interglas 02037, finish FE 800, PW), width 5 cm/100см
Glass fabric tape 49 g/m² (Interglas 02037, finish FE 800, PW), width 5 cm/100см
In stock
Glass fabric 163 g/m² (Interglas 92110, aero, twill weave), width 100 cm
Glass fabric 163 g/m² (Interglas 92110, aero, twill weave), width 100 cm
In stock
Glass fabric 80 g/m² (Finish FK 144, aero, plain weave), width 103 cm/1м
Glass fabric 80 g/m² (Finish FK 144, aero, plain weave), width 103 cm
In stock
Epoxy Resin HT 2 + Hardener HT 2 (45 min)
Epoxy Resin HT 2 + Hardener HT 2 (45 min)
Epoxy Resin HT 2 + Hardener HT 2 (45 minutes), set of two components
Solvent- and filler-free, transparent laminating and coating system of very low viscosity with an tack-free, glossy surface.
- Highly transparent, very light, max. slightly reddish in thicker layer
- The high degree of UV stability
- Tack-free curing even of thin layers
- Also for casting in layer thicknesses up to 5 mm in one operation
- Free of nonylphenol
Epoxy Resin HT 2 is suitable for impregnating glass, aramid, and carbon fibres* and for bonding wood, metal, foamed polystyrene, etc..
*Owing to its low surface tension the system exhibits good filler absorption properties. And it has excellent wetting properties with respect to reinforcing fibres of glass, aramid, and carbon.
Epoxy Resin HT 2 is a laminating resin of very low viscosity based on bisphenol A/F. The bisphenol F component reduces the viscosity and prevents the resin from forming crystals at low storage temperatures (less than + 5 °C).
Epoxy Resin HT 2 is diluted with a difunctional reactive compound and is free of solvents and fillers.
The system is highly transparent and yields in conjunction with finished glass fabrics (Finish FK 144/FK 800) highly transparent laminates with
good light fastness.
Processing time: 45 minutes
Mixing ratio:
100 : 48 parts by weight of resin to hardener
100 : 55 parts by volume of resin to hardener
Curing time: 24 hours
Cold curing
Material characteristics (pure resin hardened) Epoxy Resin HT2 with Hardener HT2:
| Flexural strength in MPa | 100 |
| Tensile strength in MPa | 71 |
| Impact strength in kJ/m² | 27 |
| Tensile modulus in MPa | 3.0 . 103 |
| Initial viscosity in mPas | 315 |
| Glas transition temperature in °C | 60 |
CYTOX Report on the Resin System Epoxy Resin L + Hardener L (see below under Additional Information): this system is not cytotoxic (cell-damaging), important for applications in medical technology.
Application:
Highly transparent, water-resistant laminates, above all for surfboards, snowboards, boat linings, aquarium accessories, light domes, solar cell coatings, floor finishes.
The Epoxy resin HT 2 is suitable for all common processing methods, e.g. hand lay-up operations, pressure and vacuum impregnation, press moulding, winding, etc..
Metal, wood, plastics, ceramics, etc., can be joined with high-strength bonds without the application of contact pressure. Curing takes place virtually free of shrinkage.
Hardener HT 2:
Cycloaliphatic amine that is used at room temperature. As with all cold-curing epoxy resin systems, it is also possible to apply additional hot curing at 50 °C for ten hours to enhance the mechanical and thermal properties.
Weitere Infos im eWiki.
In stock
Carbon round tube, wound, 3k-PW (Ø 28 / 25) x 1000 mm
Carbon round tube, wound, 3k-PW (Ø 28 / 25) x 1000 mm
In stock
Carbon round tube, wound, 3k-PW (Ø 24 / 20) x 1000 mm
Carbon round tube, wound, 3k-PW (Ø 24 / 20) x 1000 mm
In stock
Carbon round tube, wound, 3k-PW (Ø 12 / 10) x 1000 mm
Carbon round tube, wound, 3k-PW (Ø 12 / 10) x 1000 mm
Sold out
Carbon round tube, wound, 3k-PW (Ø 10 / 8) x 1000 mm
Carbon round tube, wound, 3k-PW (Ø 10 / 8) x 1000 mm
Sold out
Cyanoacrylate MD GLUE EL 4850, high elasticity
Cyanoacrylate MD GLUE EL 4850, high elasticity
Low viscosity instant adhesive. Stays elastic. Suitable for rubber and rubber-plastic combinations.
Storage and shelf life:
Our superglue can be stored in a cool and dark place for about 1 year (for example in the refrigerator at + 5 °C).
At room temperature about 6 months. At temperatures above 20 °C the shelf life is further reduced (e. g. in the summer months)