Epoxy Resin L + Hardener CL (60 min) kit/ 930 g

poxy Resin L + Hardener CL

715 g resin L + 215 g hardener CL

The resin system Epoxy Resin L + Hardener CL yields superior impregnating and wetting properties towards carbon, glass, aramid and natural fibres. It is especially suitable for carbon coating of automotive parts.

    Low viscosity
    Highly transparent
    High degree of UV stability
    Tack-free curing even of thin layers
    Glass transition temperature (Tg) > 90 °C (post-curing at 70 °C / 15 h)
    High static and dynamic strength (equal to Epoxy Resin L 285 with Hardener 285)
    Free of nonylphenol and DETA

Processing time: 60 minutes (100 g / 20 °C)

Mixing ratio:
100 : 30 parts by weight resin : hardener
100 : 35 parts by volume resin : hardener

The resin system is curing at temperatures over 20 °C but develops no distinctive brittleness even at curing temperatures below 20 °C (for at least 48 h). We however recommend, to improve the mechanical and physical properties, to perform a post-curing at least at 40 °C over 15 h.

It is suitable for the following processing procedures:

    Hand laminating
    Vacuum moulding
    Press moulding

Expertise for the resin system Epoxy resin L + Hardener CL: this system is not cytotoxic (cell damaging), important for applications in medical purposes!

Mechanical properties (Neat resin after curing at 1 h 23 °C + 5 h 70 °C + 5 h 80 °C)

Flexural test

Flexural strength (DIN EN ISO 178): 137 MPa
Surface strain at maximum stress: 6.8 %
Surface strain (no specimen failure): 7.0 %
Flexural modulus: 3.220 MPa

Tensile test

Tensile strength (DIN EN ISO 527): 82.8 MPa
Elongation at maximum strain: 4.9 %
Elongation at break: 4.7 %
Tensile modulus: 3.190 MPa

Compression test

Compressive strength (DIN EN ISO 604) at 6 % compression: 111 MPa


Shrinkage

Linear shrinkage (DIN EN 12617-1): 0.3 %