Glass fabric 25 g/m² (FE 600/800, plain weave) 110 cm, pack (folded)/ 2 m

• Free from nonylphenol and DETA
• Low viscosity, solvent- and filler-free
• Fast impregnation of glass, aramid and carbon fibres
• High static and dynamic strength
• Low surface tension, good adhesion and low curing shrinkage
• Ideal for bonding wood, metal, Styropor® etc.

Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.

Epoxy resin L with Hardener L has similar mechanical properties to the laminating systems commonly used in aircraft construction.

Processing time: 40 minutes (100 g / 20 °C)

Mixing ratio:
100 : 40 parts by weight Epoxy Resin L : Hardener L
100 : 45 parts by volume Epoxy Resin L : Hardener L

Curing time (at 23 °C): 24 hours, warm curing optional
Heat distortion temperature: Approx. 70 °C, up to a maximum of 80 °C with an additional 15 hours at 60 °C

Processing:
It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.

Material characteristics (pure resin cured) Epoxy Resin L with Hardener L:

CYTOX expert opinion on the Resin System Epoxy Resin L + Hardener L (see below under additional information): this system is not cytotoxic (cell-damaging), important for applications in medical technology

Epoxy Resin L + Hardener EPH 161 (90 min)

Peel ply tapes 95 g/m², 30 mm, plain weave, roll 1.m

Aramid roving 805 tex, spool

5 Minute Epoxy, kit/ 200 g kit includes 100 g resin + 100 g hardener + spatula + mixing cup + processing instructions

Carbon fibre plate (350 x 150 x 2.0 mm) (two layers carbon fabric prepreg 200 g/m², one core layer UD Carbon non-crimp fabric prepreg 0/90°, weight approx. 185 g)

5 Minute Epoxy, kits (MR 1:1) 100g